Physical | Nominal Value | Unit | Test Method |
Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Strength 2 (Yield) | 62.1 | MPa | ASTM D638 |
Tensile Strength 2 (Break) | 65.5 | MPa | ASTM D638 |
Tensile Elongation 2 (Break) | 120 | % | ASTM D638 |
Flexural Modulus 3 (50.0 mm Span) | 2310 | MPa | ASTM D790 |
Flexural Strength 3 (Yield, 50.0 mm Span) | 93.1 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
Instrumented Dart Impact (23°C, Energy at Peak Load) | 54.2 | J | ASTM D3763 |
Tensile Impact Strength 4 | 378 | kJ/m² | ASTM D1822 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 127 | °C | ASTM D648 |
Flammability | Nominal Value | Unit | Test Method |
Flame Rating - UL (1.09 mm) | V-2 | UL 94 | |
UL | Nominal Value | Unit | Test Method |
RTI Str | 130 | °C | UL 746 |
RTI Imp | 130 | °C | UL 746 |
RTI Elec | 130 | °C | UL 746 |